Dieses Produkt unterliegt den folgenden Normen:

DIN EN 28839 (Equivalent standards: BS EN 28839, ISO 8839, NF EN 28839) NF E28839

Technische Daten Daten

Stangen aus Messing, Kupfer, Aluminium, Bronze

Dieses Produkt unterliegt den folgenden Normen:

DIN EN 28839
NF E28839

Standard DIN EN 28839

Gleichwertige Normen:

BS EN 28839
ISO 8839
NF EN 28839

Specifies the mechanical properties of products: with nominal thread diameters from M 1,6 to M 39 inclusive, with metric ISO thread in accordance with ISO 261, made of copper and copper alloys or aluminium and aluminium alloys; it does not apply to products with special property requirements.

DIN/ISO 8839: Brass, Aluminium, Kuprodur. Mechanical properties.
Material		Nominal Diameter mm		Tensile Strenght Rm N/mm²	Stress at permanent set limit R_p0,2 N/mm²	Percentage elongation after fracture A_{5 %}
Symbol	Designation	Over	To	Min.	Min.	Min.
CU1	E-Cu57/Cu-ETP	-	39	240	160	14
CU2	CUZn37	-	6	440	340	11
CU2	CUZn37	6	39	370	250	19
CU3	CuZn39Pb3	-	6	440	340	11
CU3	CuZn39Pb3	6	39	370	250	19
CU4	CuSn6	-	12	470	340	22
CU4	CuSn6	12	39	400	200	33
CU5	CuNi1,5 Si	-	39	590	540	12
CU6	CuZn40MnPb	6	39	440	180	18
CU7	CuAI10Ni5Fe4	12	39	640	270	15
AL1	AIMg3	-	10	270	230	3
AL1	AIMg3	10	20	250	180	4
AL2	AIMg5	-	14	310	205	6
AL2	AIMg5	14	36	280	200	6
AL3	AISi1MgMn	-	6	320	250	7
AL3	AISi1MgMn	6	39	310	260	10
AL4	AICuMgSi	-	10	420	290	6
AL4	AICuMgSi	10	39	380	260	10
AL5	AIZnMgCu0,5	-	39	460	380	7
AL6	AIZn5,5MgCu	-	39	510	440	7
TI1	TI 99,8	-	20	290	180	30
TI2	TiAI6V4	-	39	890	820	10
Cold formed nuts are primarily made of following materials: Brass = Ms 63 = Cu Zn 37 Aluminium = AI Mg 3 Kuprodur = Cu Ni 1,5 Si
Machined bolts and nuts are made of following materials: Brass = Ms 58 = Cu Zn 39 Pb3 Aluminium = AI Mg Si 1

Tightening torques Ma in (Nm) for screws made of:
Ø	M2	M2,5	M3	M3,5	M4	M5	M6	M8	M10
Brass Ms 63 Ms 63	0,14	0,29	0,50	0,79	1,2	2,2	3,9	9	7
Aluminium AI Mg. 3	0,10	0,20	0,36	0,57	0,85	1,6	2,8	7	13
Kuprodur Cu Ni 1,5 Si	-	-	-	-	2,3	4,7	8	19,5	38

ASTM F468 F467 - Publication date: 2010 - COMPOSITION %
Copper and Copper-base alloys; Kupfer und Kupfer-Legierungen; Rame e leghe a base di rame
UNS Nr	alloy	general name	Al	Cu min	Fe max	Mn max	Ni max	P	Si	Zn	Pb max	Sn	As max
11000	110	ET copper	-	9.9	-	-	-	-	-	-	-	-	-
26000	260	brass	-	68.5-71.5	0.05	-	-	-	-	bal.	0.07	-	-
27000	270	brass	-	63-68.5	0.07	-	-	-	-	bal.	0.1	-	-
46200	462	naval brass	-	62-65	0.10	-	-	-	-	bal.	0.2	0.5-1	-
46400	464	naval brass	-	59-62	0.10	-	-	-	-	bal.	0.2	0.5-1	-
51000	510	phosphor bronze	-	bal.	0.10	-	-	0.03-0.35	-	0.3	0.05	4.2-5.8	-
61300	613	aluminium bronze	6-7.5	-	2-3	0.1	0.15	0.015	0.1	0.05	0.1	0.2-0.5	-
61400	614	aluminium bronze	6-8	88	1.5-3.5	1	-	-	-	-	-	-	-
63000	630	aluminium bronze	9-11	78	2-4	1.5	4-5.5	-	0.25	-	-	0.2	-
64200	642	aluminium silicon bronze	6.3-7.6	88.65	0.3	0.1	0.25	-	1.5-2.2	0.5	0.05	0.2	0.15
65100	651	silicon bronze	-	96	0.8	0.7	-	-	0.8-2	1.5	0.05	-	-
65500	655	silicon bronze	-	94.8	0.8	1.5	0.6	-	2.8-3.8	1.5	0.05	-	-
66100	661	silicon bronze	0.25	94	0.25	1.5	-	-	2.8-3.5	1.5	0.2-0.8	-	-
67500	675	manganese bronze	-	57-60	0.8-2	0.05-0.5	-	-	-	bal.	0.2	0.5-1.5	-
71000	710	cupro-nickel	-	74	0.6	1	19-23	-	-	1	0.05	-	-
71500	715	cupro-nickel	-	65	0.4-0.7	1	29-33	-	-	1	0.05	-	-

Aluminium-base alloys; Aluminium-Legierungen. Leghe di Alluminio
UNS Nr	alloy	general name	Al	Cr	Cu	Fe max	Mn max	Si max	Ti max	Zn max	Mg	Others El.
UNS Nr	alloy	general name	Al	Cr	Cu	Fe max	Mn max	Si max	Ti max	Zn max	Mg	each	total
A92024	2024	Aluminium 2024	bal.	0.10	3.8-4.9	0.5	0.3-0.9	0.5	0.15	0.25	1.2-1.8	0.05	0.15
A96061	6061	Aluminium 6061	bal.	0.04-0.35	0.15-0.40	0.7	0.15	0.40-0.8	0.15	0.25	0.8-1.2	0.05	0.15
A97075	7075	Aluminium 7075	bal.	0.18-0.35	1.2-2	0.5	0.30	0.40	0.20	5.1-6.1	2.1-2.9	0.05	0.15

Standard NF E28839

DIN/ISO 8839: Brass, Aluminium, Kuprodur. Mechanical properties.
Material		Nominal Diameter mm		Tensile Strenght Rm N/mm²	Stress at permanent set limit R_p0,2 N/mm²	Percentage elongation after fracture A_{5 %}
Symbol	Designation	Over	To	Min.	Min.	Min.
CU1	E-Cu57/Cu-ETP	-	39	240	160	14
CU2	CUZn37	-	6	440	340	11
CU2	CUZn37	6	39	370	250	19
CU3	CuZn39Pb3	-	6	440	340	11
CU3	CuZn39Pb3	6	39	370	250	19
CU4	CuSn6	-	12	470	340	22
CU4	CuSn6	12	39	400	200	33
CU5	CuNi1,5 Si	-	39	590	540	12
CU6	CuZn40MnPb	6	39	440	180	18
CU7	CuAI10Ni5Fe4	12	39	640	270	15
AL1	AIMg3	-	10	270	230	3
AL1	AIMg3	10	20	250	180	4
AL2	AIMg5	-	14	310	205	6
AL2	AIMg5	14	36	280	200	6
AL3	AISi1MgMn	-	6	320	250	7
AL3	AISi1MgMn	6	39	310	260	10
AL4	AICuMgSi	-	10	420	290	6
AL4	AICuMgSi	10	39	380	260	10
AL5	AIZnMgCu0,5	-	39	460	380	7
AL6	AIZn5,5MgCu	-	39	510	440	7
TI1	TI 99,8	-	20	290	180	30
TI2	TiAI6V4	-	39	890	820	10
Cold formed nuts are primarily made of following materials: Brass = Ms 63 = Cu Zn 37 Aluminium = AI Mg 3 Kuprodur = Cu Ni 1,5 Si
Machined bolts and nuts are made of following materials: Brass = Ms 58 = Cu Zn 39 Pb3 Aluminium = AI Mg Si 1

Tightening torques Ma in (Nm) for screws made of:
Ø	M2	M2,5	M3	M3,5	M4	M5	M6	M8	M10
Brass Ms 63 Ms 63	0,14	0,29	0,50	0,79	1,2	2,2	3,9	9	7
Aluminium AI Mg. 3	0,10	0,20	0,36	0,57	0,85	1,6	2,8	7	13
Kuprodur Cu Ni 1,5 Si	-	-	-	-	2,3	4,7	8	19,5	38

ASTM F468 F467 - Publication date: 2010 - COMPOSITION %
Copper and Copper-base alloys; Kupfer und Kupfer-Legierungen; Rame e leghe a base di rame
UNS Nr	alloy	general name	Al	Cu min	Fe max	Mn max	Ni max	P	Si	Zn	Pb max	Sn	As max
11000	110	ET copper	-	9.9	-	-	-	-	-	-	-	-	-
26000	260	brass	-	68.5-71.5	0.05	-	-	-	-	bal.	0.07	-	-
27000	270	brass	-	63-68.5	0.07	-	-	-	-	bal.	0.1	-	-
46200	462	naval brass	-	62-65	0.10	-	-	-	-	bal.	0.2	0.5-1	-
46400	464	naval brass	-	59-62	0.10	-	-	-	-	bal.	0.2	0.5-1	-
51000	510	phosphor bronze	-	bal.	0.10	-	-	0.03-0.35	-	0.3	0.05	4.2-5.8	-
61300	613	aluminium bronze	6-7.5	-	2-3	0.1	0.15	0.015	0.1	0.05	0.1	0.2-0.5	-
61400	614	aluminium bronze	6-8	88	1.5-3.5	1	-	-	-	-	-	-	-
63000	630	aluminium bronze	9-11	78	2-4	1.5	4-5.5	-	0.25	-	-	0.2	-
64200	642	aluminium silicon bronze	6.3-7.6	88.65	0.3	0.1	0.25	-	1.5-2.2	0.5	0.05	0.2	0.15
65100	651	silicon bronze	-	96	0.8	0.7	-	-	0.8-2	1.5	0.05	-	-
65500	655	silicon bronze	-	94.8	0.8	1.5	0.6	-	2.8-3.8	1.5	0.05	-	-
66100	661	silicon bronze	0.25	94	0.25	1.5	-	-	2.8-3.5	1.5	0.2-0.8	-	-
67500	675	manganese bronze	-	57-60	0.8-2	0.05-0.5	-	-	-	bal.	0.2	0.5-1.5	-
71000	710	cupro-nickel	-	74	0.6	1	19-23	-	-	1	0.05	-	-
71500	715	cupro-nickel	-	65	0.4-0.7	1	29-33	-	-	1	0.05	-	-

Aluminium-base alloys; Aluminium-Legierungen. Leghe di Alluminio
UNS Nr	alloy	general name	Al	Cr	Cu	Fe max	Mn max	Si max	Ti max	Zn max	Mg	Others El.
UNS Nr	alloy	general name	Al	Cr	Cu	Fe max	Mn max	Si max	Ti max	Zn max	Mg	each	total
A92024	2024	Aluminium 2024	bal.	0.10	3.8-4.9	0.5	0.3-0.9	0.5	0.15	0.25	1.2-1.8	0.05	0.15
A96061	6061	Aluminium 6061	bal.	0.04-0.35	0.15-0.40	0.7	0.15	0.40-0.8	0.15	0.25	0.8-1.2	0.05	0.15
A97075	7075	Aluminium 7075	bal.	0.18-0.35	1.2-2	0.5	0.30	0.40	0.20	5.1-6.1	2.1-2.9	0.05	0.15

Stangen aus Messing, Kupfer, Aluminium, Bronze

DIN/ISO 8839: Brass, Aluminium, Kuprodur. Mechanical properties.
Material		Nominal Diameter mm		Tensile Strenght Rm N/mm²	Stress at permanent set limit R_p0,2 N/mm²	Percentage elongation after fracture A_{5 %}
Symbol	Designation	Over	To	Min.	Min.	Min.
CU1	E-Cu57/Cu-ETP	-	39	240	160	14
CU2	CUZn37	-	6	440	340	11
CU2	CUZn37	6	39	370	250	19
CU3	CuZn39Pb3	-	6	440	340	11
CU3	CuZn39Pb3	6	39	370	250	19
CU4	CuSn6	-	12	470	340	22
CU4	CuSn6	12	39	400	200	33
CU5	CuNi1,5 Si	-	39	590	540	12
CU6	CuZn40MnPb	6	39	440	180	18
CU7	CuAI10Ni5Fe4	12	39	640	270	15
AL1	AIMg3	-	10	270	230	3
AL1	AIMg3	10	20	250	180	4
AL2	AIMg5	-	14	310	205	6
AL2	AIMg5	14	36	280	200	6
AL3	AISi1MgMn	-	6	320	250	7
AL3	AISi1MgMn	6	39	310	260	10
AL4	AICuMgSi	-	10	420	290	6
AL4	AICuMgSi	10	39	380	260	10
AL5	AIZnMgCu0,5	-	39	460	380	7
AL6	AIZn5,5MgCu	-	39	510	440	7
TI1	TI 99,8	-	20	290	180	30
TI2	TiAI6V4	-	39	890	820	10
Cold formed nuts are primarily made of following materials: Brass = Ms 63 = Cu Zn 37 Aluminium = AI Mg 3 Kuprodur = Cu Ni 1,5 Si
Machined bolts and nuts are made of following materials: Brass = Ms 58 = Cu Zn 39 Pb3 Aluminium = AI Mg Si 1

Tightening torques Ma in (Nm) for screws made of:
Ø	M2	M2,5	M3	M3,5	M4	M5	M6	M8	M10
Brass Ms 63 Ms 63	0,14	0,29	0,50	0,79	1,2	2,2	3,9	9	7
Aluminium AI Mg. 3	0,10	0,20	0,36	0,57	0,85	1,6	2,8	7	13
Kuprodur Cu Ni 1,5 Si	-	-	-	-	2,3	4,7	8	19,5	38

ASTM F468 F467 - Publication date: 2010 - COMPOSITION %
Copper and Copper-base alloys; Kupfer und Kupfer-Legierungen; Rame e leghe a base di rame
UNS Nr	alloy	general name	Al	Cu min	Fe max	Mn max	Ni max	P	Si	Zn	Pb max	Sn	As max
11000	110	ET copper	-	9.9	-	-	-	-	-	-	-	-	-
26000	260	brass	-	68.5-71.5	0.05	-	-	-	-	bal.	0.07	-	-
27000	270	brass	-	63-68.5	0.07	-	-	-	-	bal.	0.1	-	-
46200	462	naval brass	-	62-65	0.10	-	-	-	-	bal.	0.2	0.5-1	-
46400	464	naval brass	-	59-62	0.10	-	-	-	-	bal.	0.2	0.5-1	-
51000	510	phosphor bronze	-	bal.	0.10	-	-	0.03-0.35	-	0.3	0.05	4.2-5.8	-
61300	613	aluminium bronze	6-7.5	-	2-3	0.1	0.15	0.015	0.1	0.05	0.1	0.2-0.5	-
61400	614	aluminium bronze	6-8	88	1.5-3.5	1	-	-	-	-	-	-	-
63000	630	aluminium bronze	9-11	78	2-4	1.5	4-5.5	-	0.25	-	-	0.2	-
64200	642	aluminium silicon bronze	6.3-7.6	88.65	0.3	0.1	0.25	-	1.5-2.2	0.5	0.05	0.2	0.15
65100	651	silicon bronze	-	96	0.8	0.7	-	-	0.8-2	1.5	0.05	-	-
65500	655	silicon bronze	-	94.8	0.8	1.5	0.6	-	2.8-3.8	1.5	0.05	-	-
66100	661	silicon bronze	0.25	94	0.25	1.5	-	-	2.8-3.5	1.5	0.2-0.8	-	-
67500	675	manganese bronze	-	57-60	0.8-2	0.05-0.5	-	-	-	bal.	0.2	0.5-1.5	-
71000	710	cupro-nickel	-	74	0.6	1	19-23	-	-	1	0.05	-	-
71500	715	cupro-nickel	-	65	0.4-0.7	1	29-33	-	-	1	0.05	-	-

Aluminium-base alloys; Aluminium-Legierungen. Leghe di Alluminio
UNS Nr	alloy	general name	Al	Cr	Cu	Fe max	Mn max	Si max	Ti max	Zn max	Mg	Others El.
UNS Nr	alloy	general name	Al	Cr	Cu	Fe max	Mn max	Si max	Ti max	Zn max	Mg	each	total
A92024	2024	Aluminium 2024	bal.	0.10	3.8-4.9	0.5	0.3-0.9	0.5	0.15	0.25	1.2-1.8	0.05	0.15
A96061	6061	Aluminium 6061	bal.	0.04-0.35	0.15-0.40	0.7	0.15	0.40-0.8	0.15	0.25	0.8-1.2	0.05	0.15
A97075	7075	Aluminium 7075	bal.	0.18-0.35	1.2-2	0.5	0.30	0.40	0.20	5.1-6.1	2.1-2.9	0.05	0.15

Vollständige Liste der Lieferanten von Stangen aus Messing, Kupfer, Aluminium, Bronze

Diese Norm legt die mechanischen Eigenschaften von Produkten fest: mit Gewindenenndurchmessern von M 1,6 bis einschließlich M 39, mit metrischem ISO-Gewinde nach ISO 261, aus Kupfer und Kupferlegierungen oder Aluminium und Aluminiumlegierungen; sie gilt nicht für Produkte mit besonderen Eigenschaftsanforderungen.

Italy

ACCIAI SPECIALI ZORZETTO Srl

Hersteller von kaltgezogenen Stangen, Rollen und Drähten aus Karbonstahl, Edelstahl, Stahllegierungen, Automatenstahl, Titan und Aluminium.

Italy

Airoldi Metalli S.p.a.

Verteiler von Stangen aus Aluminium und Aluminium-Kupfer-Legierungen

India

Akshit Enterprise

Hersteller von Vormaterial aus Messing

Germany

AMARI Metall GmbH

Hersteller von Blechen, Platten und Stangen aus Nichteisenmetallen und Edelstahl

Switzerland

AMPCO METAL S.A.

Hersteller von Platten und Blechen, Stangen aus Nichteisenmetallen

India

Anand Steels

Hersteller von Stangen, Bleche, Draht aus Edelstahl, Sonderlegierungen und Nichteisenwerkstoffe

Bulgaria

Audax Corp Ltd.

Verteiler von Eisen- und Nichteisenmetallen

Germany

Aurubis AG

Hersteller von Draht und Stangen aus Kupfer

China

Beall Industry Group Co. Limited

Hersteller von Edelstahl, Duplex und Sonderlegierungen: Rohre, Platten, Bleche, Bänder und Stangen

India

Bishnoi Industries Pvt. Ltd

Hersteller von Stangen aus Edelstahl, Karbonstahl und Aluminium

Germany

Carl Pohle GmbH & Co. KG

Verteiler von Stangen und Blechen aus Stahl und Edelstahl

Germany

Carl Spaeter GmbH

Verteiler von Stangen und Blech aus Stahl, Edelstahl und Aluminium

Italy

EUral Gnutti SpA

Herstellung von Stangen und Profilen aus Aluminium

India

GASCO Inc

Hersteller von Röhren, Stangen und Verbindungselementen aus Kupfer und Nickel

Brazil

GGD Metals

Führender Verteiler von Stahl und Nichteisenmaterialien: Stangen aus Edelstahl, Baustahl, Aluminium, Bronze, Kupfer, Messing und Nylon

India

Great Steel & Metals

Verteiler und Exporteur von HV-Verbindungselementen. Verteiler von Vormaterial aus Edelstahl und Duplex.

Germany

Gutmann Aluminium Draht Gmbh

Hersteller von Draht, Stangen und Profilen aus Aluminium und Aluminium-Knetlegierungen

Germany

Häuselmann Metall GmbH

Verteiler von Blech, Bändern, Folien, Platten, Stangen, Profilen und Rohren aus Aluminium, Edelstahl, Kupfer und Kupferlegierungen

India

HEUBACH INTERNATIONAL

Importeur und Exporteur von Blech, Stangen, Draht, Platten aus Edelstahl, Karbonstahl, Nichteisenmetallen und Sonderlegierungen

India

Jalaram Metal Alloys

Hersteller von Stangen und Rohren aus Messing und Kupfer

Germany

MAGONTEC GmbH

Verteiler von Vormaterial aus Magnesiumlegierungen

Germany

MDS Mitteldeutsche Stahl GmbH

Verteiler von Stangen, Blech, Rohren und Bändern aus Stahl, Edelstahl, Aluminium und Messing

Italy

Metal Barre Srl

Verteiler von Stangen aus Bronze, Messing und Kupfer und Blech auch Aluminium, Kupfer und Bronze

France

METAL INDUSTRIEL

Hersteller von Halbzeugen (Rundstäbe, Vierecke, Rohre, Ringe Halbmond und Sonderformen) aus Bronze, Aluminiumbronze und Messing

India

Metalinox India

Verteiler von Stangen, Blech, Draht, Platten und Verbindungselementen aus Edelstahl, Titan, Monel und Nichteisenmaterialien

India

Metro Metal Technology

Hersteller von Blechen, Bändern, Draht und Stangen aus Messing

India

Microtech Metal Industries

Die Firma wurde im Jahr 1998 gegründet und aufgrund ihrer Erfahrung mitTechnologien für Nichteisenmetalle wird als ein führendes Unternehmen bezeichnet, in den Bereichen der Bestandteile von Kupfer- und Messinglegierungen sowie Verbindungselemente, Schrauben, Mutten und Bolzen

United Arab Emirates

Belgium